Co-pelletizing salt mixtures

ABSTRACT

Salts such as calcium and sodium chlorides are co-pelletized into composite pellets by contacting larger nuclei with finer particles in the presence of a salt solution which is substantially saturated in the salt of finer particle size and at least partially saturated in the other salt (or salts). This liquid acts as a viscous binder and binds the salts together into pellets in which the finer particles tend to be layered around the coarser nuclei. If desired, migration of part of the coarse nuclei salt toward the surface can be achieved. The pellets are easily handled without dusting and are useful e.g. for ice melting and dust control on roads.

"United States Patent [191 Capes CO-PELLETIZING SALT MIXTURES [75] Inventor: Charles E. Capes, Ottawa, Canada [73] Assignee: Canadian Patents & Development Ltd., Ottawa, Canada 22 Filed: July 17,1972

21 App1.No.:272,573

[451 Sept. 16, 1975 3,665,066 5/1972 Capes et a1. 264/1 17 3,666,523 5/1972 Nau 117/100 B 3,681,246 8/1972 Lewer et a1 23/313 X FOREIGN PATENTS OR APPLICATIONS 797,148 10/1968 Canada Primary ExaminerWilliam D. Martin Assistant Examiner-Stuart D. Frenkel Attorney, Agent, or FirmAlan A. Thomson [30] Foreign Application Priority Data Aug. 23, 1971 Canada 121156 [57] ABSTRACT 52 us. 01. 428/403; 252/70; 264/117; salts i are 264,122 427/215 pelletized into composite pellets by contacting larger 5 l I t Cl 2 C09K nuclei with finer particles in the presence of a salt sod 4/113 117 lution which is substantially saturated in the salt of '/I 6 23/313 427/415' finer particle size and at least partially saturated in the other salt (or salts). This liquid acts as a viscous binder and binds the salts together into pellets in [56] References C'ted which the finer particles tend to be layered around the UNITED STATES PATENTS coarser nuclei. If desired, migration of part of the 2,971,832 2/1961 Stewart et a1 23/313 X coarse nuclei salt toward the surface can be achieved, 9 6/1961 Schilberg 252/70 The pellets are easily handled without dusting and are 3,140,326 7/1964 Erck 264/117 useful e.g. for ice melting and dust control on roads. 3,345,443 10/1967 Ziegler et a1... 264/117 3,353,949 11/1967 Nau 71/25 X 11 Claims, 2 Drawing Figures r -PELLET ROCK SALT 5 as 2 C! B 2 0.4 1.1.1 0.

4 T T I3F o I l 1 1 1 IO 20 3O 4O 50 TIME. min.

CO-PELLETIZING SALT MIXTURES FIELD OF THE INVENTION This invention is concerned with pelletizing two (or more) salts into composite, dense strong pellets which are easily stored, handled and shipped with a minimum of dusting or caking. These composite salt pellets find use in de-icing of winter roads, in road compaction and dust control, in minimizing winter freezing of piles of sand or aggregate, and in other applications such as regeneration of certain water-softening systems.

BACKGROUND AND PRIOR ART Effluent streams from some chemical plants, e.g. the ammonia-soda (Solvay) process, contain waste or surplus salts which it would be desirable to process to avoid pollution problems. The salt as recovered from such effluent streams is often in a form very difficult to handle due to rock formation or caking or dusting or deliquescence depending on the circumstances and the salt. Thus there is a need to develop a means of utilizing waste or excess by-product salt and salt-containing effluent streams to produce a product which avoids the problems just mentioned, and which preferably has advantages in existing markets.

One relatively large volume market for calcium and sodium chlorides is the use on roads for deicing, compaction or dust control. Calcium chloride is marketed in powder or flake form for this purpose. Rock salt or crude NaCl is also sold for these applications and mixtures of discrete particles of the two salts have been used for de-icing. The mixture of sodium and calcium chlorides enables ice to be melted at lower ambient temperatures than for sodium chloride alone. The mixtures have the advantages for ice melting over calcium chloride alone of being less costly and less deliquescent. However these simple mixtures are very subject to the handling and storage problems mentioned above, as well as to settling and segregation giving a nonuniform product.

Crude CaCl itself commands a market in its own right e.g. for new road construction (compaction) and is often regarded as too costly and too difficult to handle and store for ice melting purposes. It would be desirable to have a salt product with some of the low temperature ice melting capability of CaCl but a minimum of the cost, storage and handling problems associated with its use for this purpose.

In the ammonia-soda (or Solvay) process the overall reaction is ZNaCHCaCO Na CO -iCaCl The excess salt (NaCl) used to favor the reaction (about 25-35%) appears in the calcium chloride liquor. This liquor is concentrated and CaCl recovered but only to the extent it can be readily sold, much of the liquor being wasted. The NaCl is quite insoluble in strong CaCl solutions and it appears in extremely fine crystalline form presenting a disposal problem. The recovered NaCl purity depends on the preceding purification steps carried out. lmpure mixtures are usually discarded. New forms of salt products particularly mixtures with advantageous properties, could lead to much wider markets and enhance the economics of the whole Solvay-type processes.

Pellets of a single salt have been formed previously by a form of agglomeration (see US. Pat. No. 3,493,642 Feb. 3, 1970 Capes et al. and Canadian Pat. No. 797,148 Oct. 22, 1968 Capes et al.). Salts have been pressure compacted into uniform pellets or flakes in the past, but the process and product have disadvantages. Rock salt has been coated with an iron cyanide and about 0.5 to 4% CaCl (US. Pat. No. 3,505,234 Apr. 7, 1970 Pinckernelle et al.). Sodium chloride, calcium chloride and water have been mixed into a paste and extruded to give porous particles (see US. Pat. No. 2,988,509 June 13, 1961 Schilberg). The layered composite pellets and their production according to the present invention are believed to be an advance in the art. Advantages of the layered pellets will be discussed more fully below.

SUMMARY OF INVENTION AND DESCRIPTION OF DRAWINGS let diameter into ice, for the composite pellet andfor.

rock salt.

The method comprises a. providing nuclei for the pellets by one of i. the use of coarse particles of one or more salts, and ii. an initial agglomeration of fine salt particles; b. contacting the nuclei with fine particles of one or more salts in the presence of a dispersed binder liquid which is a solution of at least one of said salts.

and initially substantially saturated at least with respect to the salt or salts of finer particle size;

c. during said contacting subjecting the mixture to a pellet-forming operation causing layering of said fine particles about said nuclei and complete saturation of the binder liquid solution of initially incomplete;

(1. recovering pellets from the mixture; and

e. removing liquid from the pellets.

DETAILED DESCRIPTION AND PREFERRED EMBODIMENTS For deicing, one preferred product is a co-pelletized mixture of coarse CaCl particles eg in flake or chip form acting as nuclei, with NaCl fines layered around these nuclei. A preferred binder liquid is the underflow from a salt settler following the evaporators in the calcium chloride recovery circuit of a Solvay-type process plant. This liquid is a viscous solution saturated with NaCl and containing about 40% by weight of CaCl (about -95% saturated in CaCl Such a binder liquid is desirable from the standpoint of being saturated in the component of finer particle size so that any leaching or dissolution is mainly serving to decrease the coarser particle or nuclei size (and decrease the difi'erence in particle size). The viscosity is also very appropriate for pelletizing these mixtures. Other advantages will be apparent from the Examples.

A satisfactory mixed pellet can also be made by agglomerating the fine NaCl precipitate with same com posite binder solution (no CaCl nuclei) in stages to form nuclei and layers thereon. A reasonably strong pelletized product which does not cake or dust and is readily handled results.

A composite non-uniform cross-section pellet of a on dried pellet) but these limits may be varied for other systems. Pellets of the order of one-eight inch to Onefourth inch diameter can be formed continuously with this system.

major amount of NaCl and a minor amount of CaCl is 5 The preferred pellets for road de-icing use, will be of a preferred product. Usually at least about 5% CaCI is non-uniform cross-section, having a nucleus of CaCl needed for effective de-icing with about 20-30% preor rock salt (NaCl) with surrounding layers containing ferred. both NaCl and CaCl In the Examples, some of the nu- The composite binder liquid should contain a mixcleus salt has dissolved and migrated to the surface on ture of dissolved salts preferably corresponding to the drying leaving internal void space (about 30-40% by mixture being pelletized. Non-uniform leaching of feed vol.). For best results at low ambient temperatures the I particles and desired deposition of bridges can be consurface layer will be of greater CaCl content than laytrolled by adjusting the composite salt binder solution. ers more removed from the surface. Completely saturated binder liquids can be used to The following Examples illustrate the process and avoid any leaching during pelletizing. This gives the pelletized product in more detail without limiting the most simply-controlled operation. The viscosity of the invention thereto. binder is important for good pelletizing with high viscosities usually being advantageous in commercial- EXAMPLE 1 scale pelletizing operations. Some adjustment of the A series of 14 experiments were carried out using the viscosity can be made by control of solute concentrafollowing materials: tions and temperatures. It is preferred that the liquid be Nacl Fines (97 99% Nacl) size anaysisz saturated with respect to the finer particle size salt and W Mm w at least 35-40% saturated with respect to the coarser 165% +70 0.2! 60.2% size component. The binder liquid Will usually contain +100 Q15 933% approximately 20-45% wt. of dissolved salt. +140 0.11 100% The amount of binder liquid used relative to the Coarse CaCl (Commercial Flake 78% CaCl size analysis:

Wt "/0 solids, 1s not crltical and optimum amounts Will depend +40 mm 6.8% on the particular system, concentration, temperature, +2.8 mm 34.0% viscosity, particle size, pellet size desired etc. Normally lg: 22;; from about 8 to about 40% by wt. of binder liquid I mm 80:5% based on wt. of total solids will be suitable, the lower mm 192% part of the range being used with large particles and nu- Wpmmmmely 005-010 mm clei and thin outer layers of fines. W Composition (wt Density Wet pelletizing is one mode of forming the pellets NaCl CaCl /cm which has been found advantageous. This technique A 2: 2: 3? involves carrying out the agglomeration and pellet for- 3 Salt 5 0,8 423 mation in or under a second immiscible liquid e.g. an f C purified brine 26.7 0 1.20 Inert Organlc Solvent Such as a hydrocarbon Advan' *Su ematants of specified CaCl circuit streams in Solvay process. tages include less sticking, less snowballing (easier size Control), better mixng and less dust p See 40 Pellet formation was accomplished in a lO-inch- Ra 797,148 Oct 22, 1968 Capes ct diam. balling pan with 3 inch deep sides mounted to roal. tate to horizontal. The inside surface was lined with While calcium Chl ride-Sodium rid mixture are fine screen to provide friction to establish the correct of P y concern, other Salt mixtures can also be 1 45 tumbling action in the load. Four of the experiments letized according to the invention. Examples include were carried out wet under a blanket of hydrg- Naci KC] and Caclz 2 4 mixtures- Mixtures of carbon liquid such as Varsol (trademark for aliphatic salts useful as fertilizers can also be pelletized accordhydrocarbon solvent) In the dry tests the inside uring to the invention. faces were continuously scraped with a blade simulat- The process Will be described in detail With reference ing the craping action of the plows in a commercial to the Preferred g Product P p during y disc pelletizer. The pan revolved at 40-60 rpm for the product salts and streams from the CaCl circuit of a d tests, d at 6() 8() rpm f h tests yyp Process Plant The Caclz was available in The experiments were carried out batchwise with the form of impure coarse flake of about about 100-200 g powder, and the binder liquid was inameter. The NaCl fines were about 0.1-0.3 mm size t d ed as a spray from above the pan. Nuclei were and at least 95% NaCl. A salt settler underflow liquor formed or introduced as a first step i.e., a small proporf den i y 14 g/ 42% Wt Cacl2 and (18% Wt Cl tion of the solids were first formed into nuclei (or is a typical preferred binder pern n iquid coarse CaCl used directly as nuclei) and the balance Rotating disc, pan or drum pelletizers may b used, of the powder was layered onto these nuclei) to form with the nuclei (usually CaCl added first, followed by the final pellets. Easily handled pellets of one-eighth to the fines (NaCl) and a spray of binder liquid. About one-fourth inch diameter were formed in each case. 10-35 wt. of binder liquid was found suitable (based The results are summarized in Table 1.

TABLE 1 Test Binder Approx. Wt. Wt. Water Comments on Pellets (Dry) Number Material Pellctized Liquid Liquid Used Wet Pellets l* NaCl fines A 23-31 l5-2()% Low strength, dusting 2 Nzlcl fines A 23-31 15-20% TABLE l- Continued Test Binder Approxv Wt. Wt. Water Comments on Pellets (Dry) Number Material Pelletized Liquid Liquid Used Wet Pellets 3* I part coarse CaCl B 15 about 10% strong, non-dusting 4 parts NaCl fines 4 1 part coarse CaCl. B 15 about 10% {4 parts NaCl fines 5* NaCl fines B 23-31 15-20% acceptable strength, non-dusting 6* NaCl fines ball- A 23-31 15-20% strong pellets milled overnight 7 1 part coarse CaCl B, mixed in 15 about 10% medium strength. acceptable 4 parts NaCl fines equal propor tions with water 8 1 part course CaCl C 15 about 10% low strength, some dusting 4 parts NaCl fines 9 1 part coarse CaCl B 15 about 10% strong. non-dusting 4 parts NaCl fines l 1 part coarse CaCl B 15 about 10% {4 parts NaCl fines l l 1 part coarse CaCl B 15 about 10% {'4 parts NaCl fines 12 1 part CaCl fines l20% no pellets, solid cake 3 parts NaCl fines B 23-31 on heating l3 1 part CaCl fines B 15 about strong, non-dusting 4 parLs coarse CaCl parts NaCl fines 14 1 part CaCl fines 1 part coarse CaCl B 2228 about 14-18% strong pellets if ambient 6 parts NaCl fines but not high temperature drying processed wet about 0.05% iron oxide powder blended in to colour. 1% sodium nitrite 1% sodium hexametaphosphate}added as fine powder dispersed in binder liquid for anti-corrosion. some difliculty in nucleating the mixture on pun; would be difficult to carry out on large-scale, continuous operation.

Preferred formulations were tests 3, 4, and 9-1 1 and 13 in Table 1 where coarse CaCl acted as nuclei. It was found the pellet formation was more easily stabilized in these tests tending to make continuous production attainable. Experience with finer NaCl powder i.e. top size 50 mesh and at least 25% wt. minus 200 mesh, indicates a stable pelleting operation is more easily attainable than for coarser powder. With such coarser powder a layering process on CaCl nuclei is preferred.

The strength of the pellets was found to increase as the CaCl content of the binder liquid increased. Thus liquid B with about 40% CaCl content .yielded very good pellets in tests 3, 4, 5, 9, 1O andl 1. When binder liquid B was diluted 100% with water in test 7, the product was weaker, but acceptable. However liquid A in tests 1 and 2 and liquid C in test 8 gave pellets which were weak enough to lead to considerable dusting. These results indicate that a preferred binder liquid contains about 20-45% wt. CaCl Tests 9, l0 and 11 illustrate the use of pigment to produce a coloured pellet (advantageous for marking or de-icing evaluation), and the incorporation of corrosion inhibitor-type compounds. Tests 12, 13 and 14 illustrate the use-of fine CaCl available for instance from CaCl flaking operation.

The binder liquids A-C used in these tests were saturated with respect to NaCl but not CaCl Some of the pellets, after drying, were found to have small cavities in their centres where part of thecoarse CaCl used as nuclei had dissolved before or during drying (and been deposited nearer to the surface). This is primarily due to the large increase in CaCl solubility as the temperature is raised. When the coarse CaCl was replaced by fine CaCl in test 12, the faster dissolution rate of the fines meant that the pellets liquified on drying. Thus test 12 was a failure in the sense that drying at elevated temperature caused the balls to flow and cake. This problem was solved by replacing only 20% of the coarse CaCl by these fines as in Test 13, giving pellets that dried satisfactorily.

Very interesting pellets were obtained in test 14 in EXAMPLE 2 Composite CaCl NaCl pellets were prepared as in Example 1 from 25 wt. coarse CaCl and wt.

fine NaCl, the binder liquid being saturated in NaCl' and unsaturated with but containing about 42% wt. CaCl The amount of binder liquid used was about 15% wt. of the undried pellet. The pellets were about one-fifth of an inch in diameter and contained internal voids, giving a bulk density of 0.77 gm/cc or 48 lb/ft (rock salt (NaCl) of equivalent size has a bulk density of about 1.17 gm/cc or 73 lb/ft Pellet density averaged about 1.45 gm/cc compared to 2.16 for rock salt. Average pellet void space was about 36% by volume. It was evident that some CaCl had migrated to the pellet surface on drying.

Fromphase diagrams, and solubility and freezing curves, solid NaCl, 25% CaCl 75% NaCl, and CaCl may be in contact with solution phase at temperatures not lower than -6F, -6.5F and 57F respectively. Thus it appears that major amounts of CaCl blended with NaCl are required to significantly lower the minimum melting temperature.

An evaluation of these CaCl NaCl pellets compared to rock salt in melting ice was carried out. The penetration (or melting) into ice was measured as follows. Ten cylindrical ice cubes were lined up side by side in a freezer set at the required temperature. Mirrors reflecting a scale behind each cube allowed the penetration to be followed visually. Single composite pellets, or pieces of rock salt (0.2 inch diam.) were placed on the upper ice surface and the penetration measured as a function of time. The quoted air temperature was constant around the cubes to within i 1F. The average penetration for 10 cubes was determined and plotted in FIG. 1 for both the composite pellets and rock salt.

FIG. 2 is derived from FIG. 1 and shows the time required to penetrate a constant depth of 0.2 inch. In melting roadway ice, this is a reasonable choice for depth since the pellet or piece is then well-embedded in the surface and no longer vulnerable to being removed by traffic in a highway situation.

It is evident from these two Figures that the penetration rate for the composite pellet was greater than for rock salt, and the pellet was capable of melting ice at lower temperatures than the rock salt. The difference observed particularly in FIG. 2 is more than would be expected from the minor difference in minimum melting temperature (0.5F) from phase diagram consideration. Thus some melting with the composite pellets is found to occur at temperatures below -6.5F, presumably because the CaCl near the surface is preferentially leached out of the pellet. In other words higher ratios of CaCl to NaCl than present in the whole pellet, initially dissolve from the surface giving an initial benefit in cold weather operation well beyond the overall expected CaCl contribution.

It is interesting in FIG. 1 that the lines for the pellets extrapolate at zero time to penetrations of about 0.1 inch while the NaCl lines extrapolate to close to the origin. This indicates that the initial rate of penetration of the pellet is very high apparently due in part to the positive heat release involved in the hydration of the CaCl component of the pellet. Using Intemational Critical Tables" it was calculated that the heat release on dissolution of these pellets would be sufficient for the pellet to penetrate to about one half its diameter. By contrast, rock salt absorbs heat on going into solution and no such effect would be expected.

In addition since the bulk density of the pellets is about two-thirds that of the rock salt, for a constant weight of chemical, the composite will contain about 50% more pellet units than the rock salt. In road deicing, the number of holes drilled through the ice to pavement is important in producing a clear surface and one would therefore expect that the loading (pounds per lane mile) required for clearance would be less with these pellets than with rock salt of comparable size. Preliminary road testng of this product shows this to be the case.

The composite pellets have a further advantage over an equivalent mechanical mixture of particles of CaCl and of NaCl when used below the eutectic of NaCl, since the individual pieces of CaCl and NaCl may land at points relatively distant from each other and at these temperatures only the melting capacity of the fewer CaCl pieces would be realized.

Composite pellets of different fertilizer salts of different properties can be formed in the same fashionand with control of particle size, surface layers, nuclei, binder liquid, void space and migration on drying etc.

equivalent results obtained.

I claim:

1. Composite layered pellets of non-uniform crosssection each comprising a nucleus including a coarse particle of calcium chloride, surrounded by at least one layer of finer particles comprising sodium chloride, the particles being bonded together by salt bridges formed from a binder liquid solution of said salts on removal of the liquid, and migrated calcium chloride having formed increased calcium chloride content in the surrounding layer or layers, the calcium chloride being present in about 530% wt.

2. The pellets of claim 1 containing hydrates of CaCl formed from aqueous binder liquid and CaCl on standing at ambient temperature.

3. The pellets of claim 1 containing about 30-40% internal void space.

4. A method of forming non-uniform cross-section composite layered pellets containing calcium chloride and sodium chloride comprising:

a. providing as pellet nuclei coarse particles of calcium chloride in amounts from about 5-30% wt.,

b. contacting the nuclei particles with fine particles comprising sodium chloride,

c. dispersing an aqueous binder liquid among the particles, the amount of binder liquid being of the order of 10-35% wt. based on dried pellet, the liquid being substantially saturated with sodium chloride and at least 40% saturated but not completely saturated with calcium chloride, (1. balling the mixture with a tumbling action causing the fine particles to layer on the coarse calcium chloride, y

e. evaporating the aqueous liquid causing migration of some nuclei calcium chloride into surrounding layers and deposition of salt bonds, and

f. recovering composite layered pellets having cal cium chloride deposited among the sodium chloride.

5. The method of claim 4 wherein the fine particles are added in stages with successive layers being formed.

6. The method of claim 4, wherein the coarse salt is .CaCl flakes from the CaCl recovery circuit of a Solvay process plant and'the finer salt is NaCl byproduct from the same circuit.

7. The method of claim 4 wherein the binder liquid is a salt settler underflow from the CaCl recovery circuit of a Solvay process plant.

8. The method of claim 4, wherein the binder liquid contains about 20 to about 45% by wt. CaCl 9. The method of claim 4, wherein the following operation is carried out in a blanketing liquid which is immiscible with the binder liquid.

10. The method of claim 4 wherein the coarse calcium chloride is about l-4 mm. diameter and the finer sodium chloride about 0.1-0.3 mm. diameter.

11. The method of claim 4 wherein the diameter of the coarse calcium chloride is of the order of 10 times that of the sodium chloride. 

1. COMPOSITE LAYERED PELLETS OF NON-UNIFORM CROSS-SECTION EACH COMPRISING A NUCLEUS INCLUDING A COARSE PARTICLE OF CALCIUM CHLORIDE, SURROUNDED BY AT LEAST ONE LAYER OF FINER PARTICLES COMPRISING SODIUM CHLORIDE, THE PARTICLES BEING BONDED TOGETHER BY SALT BRIDGES FROM A BINDER LIQUID SOLUTION OF SAID SALTS ON REMOVAL OF THE LIQUID, AND MIGRATED CALCIUM CHLORIDE HAVING FORMED INCREASED CALCIUM CHLORIDE CONTENT IN THE SURROUNDING LAYER OR LAYERS, THE CALCIUM CHLORIDE BEING PRESENT IN ABOUT 5-30% WT.
 2. The pellets of claim 1 containing hydrates of CaCl2 formed from aqueous binder liquid and CaCl2 on standing at ambient temperature.
 3. The pellets of claim 1 containing about 30-40% internal void space.
 4. A method of forming non-uniform cross-section composite layered pellets containing calcium chloride and sodium chloride comprising: a. providing as pellet nuclei coarse particles of calcium chloride in amounts from about 5-30% wt., b. contacting the nuclei particles with fine particles comprising sodium chloride, c. dispersing an aqueous binder liquid among the particles, the amount of binder liquid being of the order of 10-35% wt. based on dried pellet, the liquid being substantially saturated with sodium chloride and at least 40% saturated but not completely saturated with calcium chloride, d. balling the mixture with a tumbling action causing the fine particles to layer on the coarse calcium chloride, e. evaporating the aqueous liquid causing migration of some nuclei calcium chloride into surrounding layers and deposition of salt bonds, and f. recovering composite layered pellets having calcium chloride deposited among the sodium chloride.
 5. The method of claim 4 wherein the fine particles are added in stages with successive layers being formed.
 6. The method of claim 4, wherein the coarse salt is CaCl2 flakes from the CaCl2 recovery circuit of a Solvay process plant and the finer salt is NaCl byproduct from the same circuit.
 7. The method of claim 4 wherein the binder liquid is a salt settler underflow from the CaCl2 recovery circuit of a Solvay process plant.
 8. The method of claim 4, wherein the binder liquid contains about 20 to about 45% by wt. CaCl2.
 9. The method of claim 4, wherein the following operation is carried out in a blanketing liquid which is immiscible with the binder liquid.
 10. The method of claim 4 wherein the coarse calcium chloride is about 1-4 mm. diameter and the finer sodium chloride about 0.1-0.3 mm. diameter.
 11. The method of claim 4 wherein the diameter of the coarse calcium chloride is of the ordEr of 10 times that of the sodium chloride. 